Alloy MP35N® (AMS 5844/AMS 5845/ NACE MR0175)

Chemical Composition Limits

Weight %

Ni

Co

Cr

Mo

Ti

Fe

Si

Mn

P

B

S

C

MP35N®

33-37

Bal

19-21

9-10.5

1 max

1 max

0.15 max

0.15 max

0.015 max

0.010 max

0.010 max

0.03 max

MP35N® is a registered trademark of SPS Technologies Inc.

MP35N® is a multi-phase alloy containing Nickel, Cobalt, Chromium and Molybdenum with a unique range of properties - ultra high strength, toughness, bio-compatibility and corrosion resistance. It is produced by vacuum induction melting and vacuum arc re-melting (VIM-VAR) and is then strengthened by work hardening and aging, giving hardness's of up to 55-60 Rockwell C and strength levels as high as 260-300 KSI.

Due, to this unique combination of properties, MP35N® has many applications in such industries as oil and gas, aerospace and medical. MP35N can be effectively used at cryogenic temperatures without embrittlement and maintain its properties at temperatures up to 600°F, and is also suitable for medical implants and orthodontic/prosthetic devices.

MP35N® is able to resist corrosion to most mineral acid, hydrogen sulfide and seawater environments whilst exhibiting excellent resistance to stress corrosion cracking and hydrogen embrittlement, even at high strength levels. NACE MR0175 allows a hardness of up to 51 HRC for material that has been work strengthened and aged by one of the processes listed in the table below.

Anita Steel & Metals supplies MP35N® in round bar certified to either AMS 5844 (0.270" - 1.520" diameter) or NACE MR0175 (0.5" - 2.5" diameter), as well as sheet, strip and plate products suitable for medical applications.

Typical Mechanical Properties

Material

Condtion

Ultimate Tensile Strength ksi

0.2 % Yield Strength ksi

Elongation %

Reduction of Area %

Hardness HRC

MP35N ®
AMS 5844

Solution Heat Treated and Work Strengthened

255

225

12

50

45

MP35N®
AMS 5845

Solution Heat Treated and Work Strengthened and Aged

260

230

8

35

38 min


AMS 5844 is Solution Treated and Cold Worked. The AMS specification only requires that the hardness shall not be lower than 38 HRC or equivalent. However other typical mechanical properties of AMS 5844 are detailed above.

Material

Condtion

Tensile Strength ksi

Yield Strength ksi

Elongation %

Reduction of Area %

Hardness HRC

MP35N®
NACE MR0175

Age @ 1300°F/ 4 hrs

220

210

10

40

51 max

MP35N®
NACE MR0175

Age @ 1350°F / 4hrs

210

200

10

40

51 max

MP35N®
NACE MR0175

Age @ 1425°F / 6hrs

190

180

10

40

51 max

MP35N® Properties as per NACE MR0175 - Cold Drawn - Reduced Strength (min properties, round bar under 2" dia)


Availability
Alloy MP35N® is available in Round Bar, Tube, Wire, Sheet and Plate. For all stock availability contact Sales.

Specifications
UNS R30035

AMS 5758 - MP35N® VIM-VAR Bar
Solution heat treated @1900-1925°F for 4 to 8 hours

AMS 5844 - MP35N® VIM-VAR Bar
Solution heat treated @1900-1925°F for 4 to 8 hours and Work Strengthened

AMS 5845 - MP35N® VIM-VAR Bar
Solution heat treated @ 1900-1925°F for 4 to 8 hours, Work Strengthened & Aged @ 1000-1200°F for 4 hours

NACE MR0175
ASTM F-562 - Surgical Implant Applications
BS 7252-6 Surgical Implant Applications
ISO 5832-6 Surgical Implant Applications